Arkema Group Orgalloy® R 60ES Nylon 6 Alloy (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® R 60ES Nylon 6 Alloy (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Rigid polyamide 6 alloy: easy to process, low moisture absorption, chemical resistance (no known solvents). Blow extrusion grade for technical films: thermal resistance, barrier to gases and aromas, mechanical properties.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.03 g/cc	0.0372 lb/in³
Water Absorption	3.3 %	3.3 %
Moisture Absorption at Equilibrium	1.3 %	1.3 %	Humidity Absorption
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 235 °C	2.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	50.0 MPa	7250 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	3.4 %	3.4 %	50 mm/min
Tensile Modulus	2.30 GPa	334 ksi	1 mm/min
Tensile Creep Modulus, 1 hour	2030 MPa	294000 psi
Tensile Creep Modulus, 1000 hours	870 MPa	126000 psi

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Deflection Temperature at 0.46 MPa (66 psi)	130 °C	266 °F
Deflection Temperature at 1.8 MPa (264 psi)	75.0 °C	167 °F
Vicat Softening Point	129 °C	264 °F	50°C/hr; 50N
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	2.5 @Frequency 100 Hz	2.5 @Frequency 100 Hz
	3.1 @Frequency 1e+6 Hz	3.1 @Frequency 1e+6 Hz
Dielectric Strength	38.0 kV/mm	965 kV/in
Dissipation Factor	0.025 @Frequency 1e+6 Hz	0.025 @Frequency 1e+6 Hz
	0.062 @Frequency 100 Hz	0.062 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V