Arkema Group Orgalloy® LE 6006 Nylon Alloy, 6% Glass Fiber Reinforced (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® LE 6006 Nylon Alloy, 6% Glass Fiber Reinforced (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LE series, flexible polyamide alloys: processability on PE screw, low moisture absorption, chemical resistance (no known solvents).6% glass fiber reinforced. Medium stiffness, good thermomechanical resistance. Suited to injection molding.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0383 lb/in³
Water Absorption	6.0 %	6.0 %
Moisture Absorption at Equilibrium	1.6 %	1.6 %	Humidity Absorption
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 235 °C	2.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	46.0 MPa	6670 psi	50 mm/min
Elongation at Break	27 %	27 %	Nominal Strain; 50 mm/min
Tensile Modulus	1.90 GPa	276 ksi	1 mm/min

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Deflection Temperature at 0.46 MPa (66 psi)	195 °C	383 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V