Arkema Group Orgalloy® R 6600 Nylon 66 Alloy, Rigid Grade (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® R 6600 Nylon 66 Alloy, Rigid Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rigid polyamide 6.6 alloy: easy to process, low moisture absorption, chemical resistance (no known solvents).ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Water Absorption | 3.0 % | 3.0 % | |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | Humidity Absorption |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 275 °C |
18 g/10 min @Load 4.76 lb, Temperature 527 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 3.4 % | 3.4 % | 50 mm/min |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min |
| Tensile Creep Modulus, 1 hour | 2140 MPa | 310000 psi | |
| Tensile Creep Modulus, 1000 hours | 920 MPa | 133000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 1.9 @Frequency 100 Hz |
1.9 @Frequency 100 Hz |
|
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | |
| Dissipation Factor | 0.017 @Frequency 1e+6 Hz |
0.017 @Frequency 1e+6 Hz |
|
| 0.025 @Frequency 100 Hz |
0.025 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Northstar Polymers MNB-013 Prepolymer
- Johnson Matthey Mattiflux 3A Brazing Flux Paste
- SABIC Innovative Plastics Valox® 553 PBT+PC
- Shandong Rike Chemical HELIâ„¢ HPA-600 PVC Foaming Regulator
- Teknor Apex APEX® 3710-85NT1 Polyvinyl Chloride, Flexible
- Teknor Apex Sarlink® 4465 Thermoplastic Elastomer
- Covestro Makrolon® 6465 Polycarbonate, Injection Grade
- LNP Konduit® OTF-212-11 BK8-115 Polyphenylene Sulfide, Proprietary Filler (discontinued **)
- Arkema Group Orgalloy® RS 60E10 Nylon 6 Alloy, Rigid Grade (Conditioned)
Copyright © lookpolymers.com All Rights Reserved