- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyphenylene Sulfide (PPS)
- Samsung Cheil Industries Infino® XP-2140 PPS
Samsung Cheil Industries Infino® XP-2140 PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® XP-2140 PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Temperature 23.0 °C |
0.020 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.010 cm/cm @Thickness 3.20 mm |
0.0025 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 157 MPa | 22800 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 226 MPa | 32800 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 12.7 GPa | 1850 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 3.17 mm |
1.84 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C @Thickness 6.40 mm |
518 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm @Temperature 23.0 °C |
1.00e+16 ohm-cm @Temperature 73.4 °F |
50% RH; ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9855B TPE, ABS/PC Overmold
- Qualchem Danamid FCF-20 Polyamide 6, 20% Carbon Fiber
- Overview of materials for Nylon 66, 30% Glass Fiber Filled
- Laurel BioComposite Bio-Resâ„¢ 20% Composite in HDPE
- Michelman® DigiPrime® 1500LA Primer
- Solvay Specialty Polymers Polymist® XPP 552 Polytetrafluoroethylene (PTFE)
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Sheet (0.031" thick)
- A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene
- Cossa Polimeri ESTABLEND PA 6000 ABS / Nylon 6 Blend
- Clariant Renol PA113G13X050 Nylon 66, 13% Glass Fiber, Heat Stabilized, Lubricated, Improved Ductility
Copyright © lookpolymers.com All Rights Reserved