Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer	Arkema
Trade Name	Appryl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Appryl® CWE 1020 Polypropylene, 20% Talc Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Compound of a PP copolymer and 20% aesthetic talc. This grade has been specially developed for interior trim automotive applications, that required an excellent scratch resistance associated with a high modulus. It is UV stabilized.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in³
Melt Flow	15 g/10 min @Load 2.16 kg, Temperature 230 °C	15 g/10 min @Load 4.76 lb, Temperature 446 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	31.0 MPa	4500 psi	50 mm/min
Elongation at Break	15 %	15 %	Nominal Strain; 50 mm/min
Elongation at Yield	4.5 %	4.5 %	50 mm/min
Tensile Modulus	2.17 GPa	315 ksi	1 mm/min
Charpy Impact, Notched	0.520 J/cm²	2.47 ft-lb/in²
	0.300 J/cm² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Melting Point	163 °C	325 °F	10°C/min
Deflection Temperature at 0.46 MPa (66 psi)	114 °C	237 °F
Deflection Temperature at 1.8 MPa (264 psi)	58.0 °C	136 °F
Vicat Softening Point	93.0 °C	199 °F	50°C/hr; 50N