Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Direct Formed (Unverified Data**)
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Direct Formed
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 75 - 85 | 75 - 85 | ASTM D785 |
| Tensile Strength, Ultimate | 43.4 MPa @Temperature 260 °C |
6300 psi @Temperature 500 °F |
ASTM D1708 |
| 79.5 MPa @Temperature 23.0 °C |
11500 psi @Temperature 73.4 °F |
ASTM D1708 | |
| Tensile Strength, Yield | 24.4 MPa @Strain 1.00 % |
3540 psi @Strain 1.00 % |
ASTM D95 |
| 125.8 MPa @Strain 10.0 % |
18250 psi @Strain 10.0 % |
ASTM D95 | |
| Elongation at Break | 7.8 % @Temperature 260 °C |
7.8 % @Temperature 500 °F |
ASTM D1708 |
| 11 % @Temperature 23.0 °C |
11 % @Temperature 73.4 °F |
ASTM D1708 | |
| Flexural Strength | 52.0 MPa @Temperature 260 °C |
7540 psi @Temperature 500 °F |
ASTM D790 |
| 86.2 MPa @Temperature 23.0 °C |
12500 psi @Temperature 73.4 °F |
ASTM D790 | |
| Flexural Modulus | 1.48 GPa @Temperature 260 °C |
215 ksi @Temperature 500 °F |
ASTM D790 |
| 2.4463 GPa @Temperature 23.0 °C |
354.80 ksi @Temperature 73.4 °F |
ASTM D790 | |
| Compressive Modulus | 2.3152 GPa @Temperature 23.0 °C |
335.79 ksi @Temperature 73.4 °F |
ASTM D695 |
| Izod Impact, Notched (ISO) | 4.905 kJ/m² | 2.334 ft-lb/in² | ASTM D256 |
| Coefficient of Friction | 0.24 | 0.24 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.90 µm/m-°C @Temperature 23.0 - 260 °C |
2.72 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Decomposition Temperature | 616 °C | 1140 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 240 |
Users viewing this material also viewed the following:
- Radici Heraflex® A 80-42-90 G TPS-SEBS Thermoplastic Elastomer
- Plaskolite West Optix® CA - 51 HF General Purpose Acrylic Resin
- RheTech Products HP531-679UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Medium Scratch Resistant, 2B5A Black Ink
- LG Chemical Propane
- Mo-Sci Corporation GB-40-I Green B Filter Glass
- Special Metals INCONEL® C276 Nickel Superalloy Tubing, 30% Cold Work
- STAR Thermoplastic Alloys & Rubbers StarCLEAR CLR-1030 TPE
- Borealis BorSafe™ HE3490-IM HDPE Compound for Injection Molded Pressure Fittings
- Eurostar Starpylen MFK42AS PP, Glass/Mineral Filled, Injection Molded
- Aclo Accutech Polypropylene Homopolymer HP0334T40L Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved