- Aremco Corr-Paint™ CP2070 High Temperature Protective Coating Novolac-Epoxy, Pigment Only Filled
Aremco Corr-Paint™ CP2070 High Temperature Protective Coating Novolac-Epoxy, Pigment Only Filled
| Category | Polymer , Thermoset , Epoxy , Epoxy, High Temperature |
| Manufacturer | Aremco |
| Trade Name | Corr-Paint™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Corr-Paint™ CP2070 High Temperature Protective Coating Novolac-Epoxy, Pigment Only Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Two part, novolac-epoxy with exceptional abrasion adn corrosion resistance for continuous operations to 300°F (150°C) and intermittent use to 400°F (204°C).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | |
| Solids Content | 100 % | 100 % | weight |
| 100 % | 100 % | volume | |
| Volatile Organic Compounds (VOC) Content | 0.00 g/l | 0.00 g/l | |
| Viscosity | 800 - 1000 cP | 800 - 1000 cP | Mixed Viscosity |
| Thickness | 25.4 microns | 1.00 mil | estimated wet film thickness |
| 25.4 microns | 1.00 mil | recommended dry film thickness | |
| Storage Temperature | 4.44 - 32.2 °C | 40.0 - 90.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 149 °C | 300 °F | |
| Flash Point | >= 93.3 °C | >= 200 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 10.0 - 32.2 °C | 50.0 - 90.0 °F | Application Temperature |
| Dry Time | 5.00 hour | 5.00 hour | Touch |
| 4.00 - 8.00 hour | 4.00 - 8.00 hour | Recoat | |
| 8.00 hour | 8.00 hour | Handling | |
| Cure Time | 1440 min @Temperature 22.2 °C |
24.0 hour @Temperature 72.0 °F |
>8 Hour Air Set Required Prior to Curing |
| Shelf Life | 12.0 Month @Temperature 23.0 °C |
12.0 Month @Temperature 73.4 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Gray | |
| Dry Film Coverage ft2/gal | 1604 | at 1 mil |
| Mix Ratio | 100:42 | Novolac:Epoxy |
| 2:1 | by volume, Novolac:Epoxy | |
| Thinner | Xylene |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Dry Blend E1500 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Nilit Nilamid A3 H7 G6 30% Glass Reinforced PA66
- LG Chemical Lupox® HV-1010 General Purpose PBT, Unreinforced, High Viscosity
- SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP 2X03624H FP-F (FEP)
- DSM Novamid® 1010GN8-30 NAT PA6-GF30 FR
- A.D. Compound Adene NTJA Homopolymer 30% Talc Filled Polypropylene
- Arlon 44576R016 0.016" (0.406 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate
- Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (5 mm Molded Thickness)
- 3M 97065 General Purpose Aluminum Foil Tape
Copyright © lookpolymers.com All Rights Reserved