Aremco Aremco-Seal™ 617 High Temperature Glass Coating
| Category | Ceramic , Other Engineering Material , Ceramic/Metallic Coating |
| Manufacturer | Aremco |
| Trade Name | Aremco-Seal™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Seal™ 617 High Temperature Glass Coating.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass-filled adhesive/sealer for use with porous ceramics and refractories to 1500 ºF (816 ºC).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | |
| Solids Content | 40.5 % | 40.5 % | by volume |
| 51.3 % | 51.3 % | by weight | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 1100 - 1500 cP | 1100 - 1500 cP | |
| Thickness | 25.4 microns | 1.00 mil | recommended dry film thickness |
| 62.7 microns | 2.47 mil | estimated wet film thickness | |
| Storage Temperature | 40.0 - 90.0 °C | 104 - 194 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 816 °C | 1500 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 3.00 min @Temperature 899 °C |
0.0500 hour @Temperature 1650 °F |
Step 3 |
| 30.0 min @Temperature 93.3 °C |
0.500 hour @Temperature 200 °F |
Step 1, preceeded by >30 min. air set | |
| 60.0 min @Temperature 177 °C |
1.00 hour @Temperature 350 °F |
Step 2 | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | Cured |
| Dry Film Coverage ft2/gal | 650 | at 1 mil |
| Thinner | Water |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP EIP16020 F PP Mineral Reinforced, Extrusion Grade, Low CLTE
- Quadrant EPP Quadrant PC 1000 Extruded, Unfilled, Polycarbonate (ASTM Product Data Sheet)
- Total EVA 1005 VN 35 Ethylene Vinyl Acetate Copolymer - Blown Film
- A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Polyram RamOfin PPC371B73 Polypropylene, 73% Mineral Filled
- Dow AFFINITY™ GA 1950 Polyolefin Plastomer (POP)
- Eurotec® Tecodur® PB70 NL SV20 PBT, unfilled, flame retardant - halogen (RoHS compliant), natural
- Beijing Chemical Industry KAIFA® HN301-G20 PA6 Resin
- Beijing Ranger Chem 0164E Liquid Epoxy Resin
- 3M Nextel™ XN-513 Woven Fabric 720
Copyright © lookpolymers.com All Rights Reserved