- SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ZL003 is a compound based on PPE+PS Blend resin containing PTFE. Added features include Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0089 cm/cm | 0.0089 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.6 % | 4.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
43.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
45.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- DSM Akulon® S223-HG6U (Dry) 33% Glass Reinforced Nylon 66 (North America) (discontinued **)
- ITW Plexus Plexusâ„¢ MA1020 Methacrylate Adhesive
- Sinotek Materials ZSLZ87 Middle Carbon Graphite
- A. Schulman FORMION™ FI 330 Ionomer
- ExxonMobil Optema® TC-114 Blown Ethylene Methyl Acrylate
- Eurotec® Tecomid® NB40 GB30 NL PA6, 30% glass bead reinforced, natural
- DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&
- Fluorocarbon Rubber (FPM), Low Temperature Grade
- 3M Dyneon™ FC 2173 Fluoroelastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved