Borealis BC650MO Polypropylene Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis BC650MO Polypropylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BC650MO is a very high impact polypropylene heterophasic copolymer intended for injection molding. This product offers a good UV resistance, further enhanced by pigmentation. This grade features high impact strength, high thermal stability and very good processability. As all polypropylenes, this grade shows excellent stresscracking and chemical resistances. This grade is characterized by combination of good stiffness, good creep resistance and very high impact strength even at low temperatures. This grade is mildly nucleated to maximize the mechanical stiffness. The additive formulation provides a smooth demolding. Nucleation, good flow properties and high stiffness create a high potential for cycle time reduction. Its very good organoleptic properties allows this grade to be used with any masterbatch without discoloring problems. Applications: crates and boxes, pallets, technical parts, bottle trays, and luggage.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.904 g/cc
0.0327 lb/in³
ISO 1183
Linear Mold Shrinkage 0.010 - 0.020 cm/cm
0.010 - 0.020 in/in
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 80
80
ISO 2039-2
Tensile Strength, Yield 22.5 MPa
3260 psi
50mm/min; ISO 527-2
Elongation at Yield 5.5 %
5.5 %
50mm/min; ISO 527-2
Tensile Modulus 1.20 GPa
174 ksi
1mm/min; ISO 527-2
Charpy Impact, Notched 0.750 J/cm²

@Temperature -20.0 °C
3.57 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Puncture Energy 41.0 J

@Temperature -40.0 °C
30.2 ft-lb

@Temperature -40.0 °F
ISO 6603-2
46.0 J

@Temperature -20.0 °C
33.9 ft-lb

@Temperature -4.00 °F
ISO 6603-2
48.0 J

@Temperature 0.000 °C
35.4 ft-lb

@Temperature 32.0 °F
ISO 6603-2
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
ISO 75-2
Processing Properties Metric English Comments
Melt Temperature 230 - 260 °C
446 - 500 °F
Mold Temperature 10.0 - 30.0 °C
50.0 - 86.0 °F
Hold Pressure 20.0 - 50.0 MPa
2900 - 7250 psi
Descriptive Properties Value Comments
Injection Velocity highest possible