Amity Thermosets ATS 155 Phenolic Molding Inorganic and glass fiber Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATS 155 Phenolic Molding Inorganic and glass fiber Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:Shock resistantElectrical low lossHigh mechanical strengthHeat stableHigh electrical insulationDimensional stabilityGood mechanical tension bearing strengthGood copper adhesion Color-blackMedium/soft flow Applications: Commutators ( small motors ), etc. Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.60 - 1.70 g/cc	0.0578 - 0.0614 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.650 - 0.720 g/cc	0.0235 - 0.0260 lb/in³	IS 867-1963
Water Absorption	0.20 - 0.35 %	0.20 - 0.35 %	IS 13411-1993
Linear Mold Shrinkage	0.0030 - 0.0038 cm/cm	0.0030 - 0.0038 in/in	IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	65.0 - 75.0 MPa	9430 - 10900 psi	5 mm/min.; IS 867-1963
Shear Strength	85.0 - 95.0 MPa	12300 - 13800 psi	IS 867-1963
Izod Impact, Notched	0.600 - 0.700 J/cm	1.12 - 1.31 ft-lb/in	IS 13411-1992

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.2e+11 - 1.0e+12 ohm-cm	3.2e+11 - 1.0e+12 ohm-cm	IS 3396-1979
Surface Resistance	1.00e+11 - 3.16e+11 ohm	1.00e+11 - 3.16e+11 ohm	IS 3396-1979
Dielectric Strength	6.50 - 8.00 kV/mm @Temperature 90.0 °C	165 - 203 kV/in @Temperature 194 °F	IS 2584-1963
Comparative Tracking Index	>= 175 V	>= 175 V	2824-1975

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 180 °C	320 - 356 °F
Injection Pressure	15.68 - 34.3 MPa	2274 - 4970 psi	Mold Pressure
Cure Time	1.33 - 1.67 min	0.0222 - 0.0278 hour	per mm
Shelf Life	4.00 Month	4.00 Month	10-25°C