Americas Styrenics MC3650 High Heat Crystal Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade
Manufacturer	Americas Styrenics LLC
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Americas Styrenics MC3650 High Heat Crystal Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product CharacteristicsImproved cycle times in hard to fill partsExcellent clarity with slight blue tintFood Contact CompliantUL Classification 94HBUSP Class VITypical ApplicationsHousewaresConsumer containers, vials, jars, etc.Disposable cutleryInjection molded drink cupsInformation provided by AmericasStyrenics LLC.

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	ASTM D955
Melt Flow	13 g/10 min @Load 5.00 kg, Temperature 200 °C	13 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell L	107	107	ASTM D785
Tensile Strength at Break	44.8 MPa	6500 psi	ASTM D638
Tensile Strength	44.8 MPa	6500 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Tensile Modulus	3.17 GPa	460 ksi	ASTM D638
Flexural Strength	55.2 MPa	8000 psi	ASTM D790
Flexural Modulus	3.31 GPa	480 ksi	ASTM D790
Izod Impact, Notched	0.214 J/cm	0.400 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C	50.0 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	87.2 °C	189 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	80.6 °C	177 °F	ASTM D648
Vicat Softening Point	97.8 °C	208 °F	ASTM D1525