Quantum Composites AMC™ 8595 55% Carbon Fiber Reinforced Vinyl Ester SMC

Category	Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Composite SMC , Vinyl Ester , Vinyl Ester Sheet Molding Compound
Manufacturer	Quantum Composites
Trade Name	AMC™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Quantum Composites AMC™ 8595 55% Carbon Fiber Reinforced Vinyl Ester SMC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AMC™ 8595 is a vinyl ester engineered structural composite molding compound with continuous, unidirectional carbon fibers. It is designed for compression molding of components requiring high structural strength, light weight, and stiffness. It can also be co-molded with other ESC molding compounds such as AMC™ 8590 to provide stiffening in selected areas of the component.Form = Rolled SheetColor = Natural, BlackCarbon Fiber Content = 55% nominalCarbon Fiber Length = ContinuousAreal Weight = 1129 g/m2Information provided by Quantum Composites.

Physical Properties	Metric	English	Comments
Specific Gravity	1.50 g/cc	1.50 g/cc	ASTM D792
Water Absorption	0.11 %	0.11 %	ASTM D570
Linear Mold Shrinkage	0.00 cm/cm	0.00 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength	993 MPa	144000 psi	ASTM D638
Tensile Modulus	94.5 GPa	13700 ksi	ASTM D638
Flexural Strength	1310 MPa	190000 psi	ASTM D790
Flexural Modulus	77.9 GPa	11300 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	287 °C	549 °F	Deflection Temperature, Load not specified; ASTM D648

Processing Properties	Metric	English	Comments
Processing Temperature	132 - 149 °C @Thickness 12.7 mm	270 - 300 °F @Thickness 0.500 in	Compression Molding
Clamp Pressure	2.07 - 6.89 MPa	300 - 1000 psi
Cure Time	3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C	0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F
Shelf Life	3.00 Month @Temperature 23.9 °C	3.00 Month @Temperature 75.0 °F