Adell AJ-34 Nylon 66, 20% Glass Reinforced; High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell AJ-34 Nylon 66, 20% Glass Reinforced; High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM D790 |
| Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D695 |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Overview of materials for Polytetrafluoroethylene (PTFE), Conductive Carbon Filled
- Fiberfil® J-60/30/E/HF Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled, improved flow
- Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; HT (TH04) Temper; up to 9.5 mm Thickness (UNS C17200)
- A. Schulman POLYBATCH™ Orange 1046E Concentrate Based In Polyethylene
- ExxonMobil EXACT™ 0230 Plastomer for Multilayer Film Applications
- 3M Controltac™ 160 Graphic Film
- 3M RPF-C (0.382 g/cc) (Reinforced Polyurethane Foam) Continuous Strand Fiberglass
- LATI LARIL 13-V1 Polyphenylene Oxide (PPOm) (UL94V-1) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved