Plenco 7487 Phenolic, Granular, Transfer Molded

Category	Polymer , Thermoset , Phenolic , Phenolic/Rubber; Molded
Manufacturer	Plenco (Plastics Engineering Company)
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plenco 7487 Phenolic, Granular, Transfer Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PLENCO 07487 is a rubber modified organic reinforced phenolic molding compound offering improved mechanical strength and lower modulus. Plenco 07487 is available in black.Information supplied by Plenco.

Physical Properties	Metric	English	Comments
Bulk Density	0.550 g/cc	0.0199 lb/in³	ASTM D1895
Density	1.34 g/cc	0.0484 lb/in³	ASTM D792
Water Absorption	0.92 %	0.92 %	ASTM D570
Linear Mold Shrinkage	0.0079 cm/cm	0.0079 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell E	76	76	ASTM D785
Tensile Strength, Ultimate	34.0 MPa	4930 psi	ASTM D638
Elongation at Break	1.47 %	1.47 %	ASTM D638
Tensile Modulus	4.50 GPa	653 ksi	ASTM D638
Flexural Strength	56.0 MPa	8120 psi	ASTM D790
Flexural Modulus	3.60 GPa	522 ksi	ASTM D790
Compressive Strength	82.0 MPa	11900 psi	ASTM D695
Izod Impact, Notched	0.233 J/cm	0.437 ft-lb/in	ASTM D256
Charpy Impact, Notched	0.281 J/cm²	1.34 ft-lb/in²	ASTM D256
Impact	262	262	J/m Drop Ball Impact; PLENCO

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	217 °C	423 °F	Heat Resistance; ASTM D570D
Deflection Temperature at 1.8 MPa (264 psi)	136 °C	277 °F	ASTM D648
Oxygen Index	24.6 %	24.6 %	ASTM D2863
Shrinkage	0.39 %	0.39 %	72 hr, 120ºC; ASTM D1299

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+11 ohm-cm	2.00e+11 ohm-cm	ASTM D247
Dielectric Constant	4.5	4.5	ASTM D150
Dielectric Strength	11.5 kV/mm	292 kV/in	Short Time; ASTM D149
Dissipation Factor	0.081	0.081	ASTM D150
Arc Resistance	67 sec	67 sec	ASTM D495
Comparative Tracking Index	150 V	150 V	ASTM D3638