- Cossa Polimeri ESTAPROP H 0580 GFC Polypropylene, 40% Glass Filled
Cossa Polimeri ESTAPROP H 0580 GFC Polypropylene, 40% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 0580 GFC Polypropylene, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 40% chemically coupled glass fiberExcellent stiffness, excellent impact strengthInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D 955 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Tensile Modulus | 8.20 GPa | 1190 ksi | ASTM D 638 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature -20.0 °C |
1.87 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 1.10 J/cm @Temperature 0.000 °C |
2.06 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 1.30 J/cm @Temperature 23.0 °C |
2.44 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 140 °C @Load 5.00 kg |
284 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear (Asia Pacific)
- ExxonMobil 32 Mobil EAL Arctic Series
- A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.25 PHR Zinc Stearate
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Laminar Filler
- Dow Corning SILASTIC® LS 5-8725 FLUOROSILICONE RUBBER
- ExxonMobil Mobil Zerice 68 S Oil
- Fainplast Compounds GS 56 Flexible PVC, Injection Molding for Footwear
- Beijing Ranger Chem BLUESTAR® 1135 PBT
- Axiall 7801 Rigid PVC, Extrusion, White, High Impact Profile
Copyright © lookpolymers.com All Rights Reserved