Addiplast Addilene H 490 M10F Flame Retardant Polypropylene, 10% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant , Polypropylene, Mineral Reinforced |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene H 490 M10F Flame Retardant Polypropylene, 10% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, mineral filled, with halogensInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183/A |
| Melt Flow | 12 g/10 min | 12 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | Conditioned; ISO 868 |
| Tensile Strength at Break | 29.0 MPa | 4210 psi | Conditioned; ISO R 527 |
| Elongation at Break | 25 % | 25 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 2.30 GPa | 334 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-2/AF |
| Vicat Softening Point | 153 °C | 307 °F | ISO 306/A50 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® FL 25 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
- Polimersan Plastics POLITEF® (PTFE) with 25% Carbon
- SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer
- Momentive Performance Materials HV 3/506 Heat Cured Rubber - High Temperature
- Styron DL 470PA SB Latex
- ChevronTexaco Bright-Cut® NM Metal Working Fluid
- Fainplast Compounds PM 8725 Flexible PVC, Lead Free
- Beijing Chemical Industry KAIFA® GL2200 ABS Good Flow Grade
- BASF Polystyrol® 2712 Impact Grade Polystyrene (Europe)
Copyright © lookpolymers.com All Rights Reserved