Vyncolit Neopreg Kinel® SK4502 S8 Carbon Reinforced Molding Compound

Category Polymer , Thermoset , Epoxy , Epoxy Molding Compound , Filled/Reinforced Thermoset
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name Neopreg Kinel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit Neopreg Kinel® SK4502 S8 Carbon Reinforced Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KINEL SK4502 S8 is a long carbon fiber reinforced BMI molding compound suited for very demanding tribological applications, high speeds and temperatures even under dry running conditions. Thermal expansion similar to steel.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 0.290 g/cc
0.0105 lb/in³
ISO 60
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Water Absorption 0.19 %
0.19 %
ISO 62
Linear Mold Shrinkage 0.00040 cm/cm
0.00040 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 87.0 MPa

@Temperature 250 °C
12600 psi

@Temperature 482 °F
ISO 527-1
123 MPa

@Temperature 150 °C
17800 psi

@Temperature 302 °F
ISO 527-1
165 MPa

@Temperature 23.0 °C
23900 psi

@Temperature 73.4 °F
ISO 527-1
Elongation at Break 0.30 %

@Temperature 250 °C
0.30 %

@Temperature 482 °F
ISO 527-1
0.40 %

@Temperature 23.0 °C
0.40 %

@Temperature 73.4 °F
ISO 527-1
0.40 %

@Temperature 150 °C
0.40 %

@Temperature 302 °F
ISO 527-1
Tensile Modulus 29.0 GPa

@Temperature 250 °C
4210 ksi

@Temperature 482 °F
ISO 527-1
32.0 GPa

@Temperature 150 °C
4640 ksi

@Temperature 302 °F
ISO 527-1
44.0 GPa

@Temperature 23.0 °C
6380 ksi

@Temperature 73.4 °F
ISO 527-1
Flexural Strength 256 MPa

@Temperature 250 °C
37100 psi

@Temperature 482 °F
ISO 178
345 MPa

@Temperature 150 °C
50000 psi

@Temperature 302 °F
ISO 178
353 MPa

@Temperature 23.0 °C
51200 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 30.0 GPa

@Temperature 150 °C
4350 ksi

@Temperature 302 °F
ISO 178
30.0 GPa

@Temperature 250 °C
4350 ksi

@Temperature 482 °F
ISO 178
32.0 GPa

@Temperature 23.0 °C
4640 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 170 MPa

@Temperature 250 °C
24700 psi

@Temperature 482 °F
ISO 604
172 MPa

@Temperature 150 °C
24900 psi

@Temperature 302 °F
ISO 604
176 MPa

@Temperature 23.0 °C
25500 psi

@Temperature 73.4 °F
ISO 604
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 275 °C
527 °F
Shrinkage -0.0600 %
-0.0600 %
Post Shrinkage; ISO 2577
Descriptive Properties Value Comments
Color Black
Molding Method Compression
Injection
Transfer