Aclo Accutech Polypropylene Homopolymer HP0339W10L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339W10L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
| Elongation at Break | 24 % | 24 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Strength | 38.0 MPa | 5510 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 0.352 J/cm | 0.660 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |
Users viewing this material also viewed the following:
- Polymer Resources PC/ABS-GP2 General Purpose PC/ABS Alloy, High Flow
- LG Chemical LUCEL N109LD POM, Chemical Resistance
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR N774 (SRF) Filler
- Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N220 Filler
- SABIC Innovative Plastics LNP VERTON MV00AS PP
- ChevronTexaco Pinnacle® 46
- Arkema Group Rilsan® BESHV Nylon 11, Blow Molding Grade (Conditioned)
Copyright © lookpolymers.com All Rights Reserved