Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Mineral Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention of stiffness at elevated temperatures. This grades also exhibits a high deflection temperature and flexural modulus. - Black: A-1565 HS BK 324Data is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.90 g/cc	0.0686 lb/in³	ISO 1183/A
Filler Content	65 %	65 %	GlassMineral
Water Absorption	0.10 % @Time 86400 sec	0.10 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 cm/cm	0.0050 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	32.4 MPa @Temperature 175 °C	4700 psi @Temperature 347 °F	ISO 527-2
	46.2 MPa @Temperature 150 °C	6700 psi @Temperature 302 °F	ISO 527-2
	91.7 MPa @Temperature 100 °C	13300 psi @Temperature 212 °F	ISO 527-2
	138 MPa @Temperature 23.0 °C	20000 psi @Temperature 73.4 °F	ISO 527-2
Tensile Strength	123 MPa	17800 psi	Conditioned; ASTM D638
	131 MPa	19000 psi	ASTM D638
Elongation at Break	1.2 %	1.2 %	Conditioned; ASTM D638
	1.2 %	1.2 %	ASTM D638
	1.0 % @Temperature 23.0 °C	1.0 % @Temperature 73.4 °F	ISO 527-2
	1.3 % @Temperature 100 °C	1.3 % @Temperature 212 °F	ISO 527-2
	1.8 % @Temperature 175 °C	1.8 % @Temperature 347 °F	ISO 527-2
	2.4 % @Temperature 150 °C	2.4 % @Temperature 302 °F	ISO 527-2
Tensile Modulus	20.7 GPa	3000 ksi	ASTM D638
	20.8 GPa	3020 ksi	Conditioned; ASTM D638
	5.10 GPa @Temperature 175 °C	740 ksi @Temperature 347 °F	ISO 527-2
	5.72 GPa @Temperature 150 °C	830 ksi @Temperature 302 °F	ISO 527-2
	15.4 GPa @Temperature 100 °C	2230 ksi @Temperature 212 °F	ISO 527-2
	19.7 GPa @Temperature 23.0 °C	2860 ksi @Temperature 73.4 °F	ISO 527-2
Flexural Strength	196 MPa	28400 psi	Conditioned; ASTM D790
	210 MPa	30500 psi	ASTM D790
	55.8 MPa @Temperature 175 °C	8090 psi @Temperature 347 °F	ISO 178
	69.6 MPa @Temperature 150 °C	10100 psi @Temperature 302 °F	ISO 178
	163 MPa @Temperature 100 °C	23600 psi @Temperature 212 °F	ISO 178
	211 MPa @Temperature 23.0 °C	30600 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	17.9 GPa	2600 ksi	ASTM D790
	18.0 GPa	2610 ksi	Conditioned; ASTM D790
	2.28 GPa @Temperature 175 °C	331 ksi @Temperature 347 °F	ISO 178
	2.48 GPa @Temperature 150 °C	360 ksi @Temperature 302 °F	ISO 178
	6.83 GPa @Temperature 100 °C	991 ksi @Temperature 212 °F	ISO 178
	9.10 GPa @Temperature 23.0 °C	1320 ksi @Temperature 73.4 °F	ISO 178
Compressive Strength	189 MPa @Thickness 13.0 mm	27400 psi @Thickness 0.512 in	ASTM D695
Shear Strength	49.6 MPa	7190 psi	Conditioned; ASTM D732
	71.0 MPa	10300 psi	ASTM D732
Izod Impact, Notched	0.320 J/cm	0.599 ft-lb/in	Conditioned; ASTM D256
	0.370 J/cm	0.693 ft-lb/in	ASTM D256
	4.10 J/cm	7.68 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	4.00 kJ/m²	1.90 ft-lb/in²	ISO 180/1A
Izod Impact, Unnotched (ISO)	32.0 kJ/m² @Temperature 23.0 °C	15.2 ft-lb/in² @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	4.40 J/cm²	20.9 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.340 J/cm²	1.62 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	17.0 µm/m-°C @Temperature 100 - 200 °C	9.44 µin/in-°F @Temperature 212 - 392 °F	TMA; ASTM E831
	20.0 µm/m-°C @Temperature 0.000 - 100 °C	11.1 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	37.0 µm/m-°C @Temperature 0.000 - 100 °C	20.6 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E831
	81.0 µm/m-°C @Temperature 100 - 200 °C	45.0 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
Melting Point	311 °C	592 °F	Peak; ASTM D3418
	311 °C	592 °F	ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi)	271 °C	520 °F	Unannealed; ASTM D648
	271 °C	520 °F	Unannealed; ISO 75-2/A

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.00e+14 ohm-cm	4.00e+14 ohm-cm	ASTM D257
Arc Resistance	125 sec	125 sec	ASTM D495
Comparative Tracking Index	600 V	600 V	UL 746

Processing Properties	Metric	English	Comments
Feed Temperature	79.4 °C	175 °F	Hopper Temperature
Rear Barrel Temperature	304 - 318 °C	579 - 604 °F
Front Barrel Temperature	316 - 329 °C	601 - 624 °F
Melt Temperature	321 - 343 °C	610 - 649 °F
Mold Temperature	135 °C	275 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
Appearance	Black
Automotive Specifications	ASTM D4000 PA121 R65 Color: BK324 Black
	ASTM D6779 PA121R65
	DELPHI M-53294 Color: BK324 Black
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	High Heat Resistance
	Low CLTE
	Low Warpage
	Lubricated
	Ultra High Stiffness
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications