Styron CALIBREâ„¢ MEGARAD 2081-6LR Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™ MEGARAD
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ MEGARAD 2081-6LR Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: CALIBREâ„¢ 2081-6LR Polycarbonate resin was developed for medical applications requiring improved resistance to lipids over standard polycarbonate resins. When exposed to a 20% intralipid emulsion solution under strained conditions, CALIBRE MEGARAD 2081-6LR exhibits significant property retention compared to standard polycarbonate. It also provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to high energy radiation (gamma or electron beam), CALIBRE MEGARAD 2081-6LR can reduce the color shift by 50% compared to general purpose polycarbonate resins. CALIBRE MEGARAD 2081-6LR has been evaluated with respect to ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.Main Characteristics:Improved lipid resistanceStabilized for high-energy radiationTransparentContains mold releaseISO 10993Applications:Medical applicationsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Water Absorption 0.32 %

@Temperature 23.0 °C
0.32 %

@Temperature 73.4 °F
Equilibrium, 50% RH; ASTM D570
0.15 %

@Temperature 23.0 °C,
Time 86400 sec
0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength at Break 68.3 MPa
9910 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 65.5 MPa
9500 psi
50 mm/min; ASTM D638
Elongation at Break 130 %
130 %
50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ASTM D638
Tensile Modulus 2.34 GPa
339 ksi
50 mm/min; ASTM D638
Flexural Strength 96.5 MPa
14000 psi
Method I (3 point load), 2.0 mm/min; ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
Method I (3 point load), 2.0 mm/min; ASTM D790
Izod Impact, Notched 8.50 J/cm

@Temperature 23.0 °C
15.9 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D256
Tensile Impact Strength 567 kJ/m²
270 ft-lb/in²
ASTM D1822
Dart Drop, Total Energy 89.3 J
65.9 ft-lb
3.39 m/sec; ASTM D3763
Abrasion 45
45
[%] Taber; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.0 µm/m-°C
37.8 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Unannealed; ASTM D648
142 °C
288 °F
Annealed; ASTM D648
Vicat Softening Point 151 °C
304 °F
Rate A (50°C/h); ASTM D1525
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D542
Haze 1.0 %
1.0 %
ASTM D1003
Transmission, Visible 71 - 85 %
71 - 85 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 60.0 Hz
3.0

@Frequency 60.0 Hz
ASTM D150
3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 50.0 Hz
0.0010

@Frequency 50.0 Hz
ASTM D150
0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150