Aclo Accutech Polypropylene Homopolymer HP0336M40L Mica Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336M40L Mica Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 4.300 GPa | 623.6 ksi | ASTM D638 |
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Flexural Modulus | 4.599 GPa | 667.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.750 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.1 °C | 178 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 5 T 20 FRG 2 PA6, 5% glass fibre, 20% mineral filling
- PolyOne Elastamax™ XL-2165 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Overview of materials for Nylon 12, 50% Glass Fiber Filled
- Huntsman IROGRAN® A 92 P 4851 Ether-Based TPU-For Cable Industry
- Wellman Wellamid® 22LN2-N Unfilled Nylon 66, Lubricated & Nucleated
- Elastron® V TPV Elastomer
- CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Dry
- BNZ Materials Marinite® I&M High Temperature Structural Insulation
- Asahi Kasei Leona® 1702 Nylon 66
- Gouda Vuurvast FLUCON 180 Dense Self Flowing Refractory Castable
Copyright © lookpolymers.com All Rights Reserved