SABIC Innovative Plastics LNP THERMOCOMP YF003S Polyester Elastomer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP YF003S Polyester Elastomer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* YF003S is a compound based on Polyester Elastomer containing Glass Fiber. Added features include; Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.54 % @Time 86400 sec |
0.54 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 15 % | 15 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.50 GPa | 218 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.20 GPa | 174 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 85.0 kJ/m² | 40.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
18.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 195 µm/m-°C @Temperature 23.0 - 60.0 °C |
108 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Molding M5240 Polyvinyl Chloride, Rigid (PVC, Rigid)
- OMG Americas GlidCop® AL-25 Dispersion Strengthened Copper
- Borealis Himod™ FT7324 . LDPE for Film
- Polyram RamOfin PPH106 Polypropylene, Injection Molding
- ExxonMobil Exxtral™ BMU130P Performance Polyolefin
- 3M AC-730 Class C-4 (168) Aerospace Sealant
- Bapolene® 4082NA Polypropylene
- AK Steel CL 2/ SAE J1392 045 XLK, Grade 45 Cold Rolled Carbon Steel, High Strength Low Alloy Steel (HSLAS)
- Bulk Molding Compounds tetra-DUR F 4306 Bulk Molding Compound
Copyright © lookpolymers.com All Rights Reserved