- Aclo Accutech Polypropylene Homopolymer HP0334G15M15CL Glass/Mineral Reinforced Coupled
Aclo Accutech Polypropylene Homopolymer HP0334G15M15CL Glass/Mineral Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334G15M15CL Glass/Mineral Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.299 GPa | 478.5 ksi | ASTM D638 |
| Flexural Strength | 69.98 MPa | 10150 psi | ASTM D790 |
| Flexural Modulus | 4.000 GPa | 580.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F |
Users viewing this material also viewed the following:
- DSM Akulon® S223-P2 Impact Modified Nylon 66 (European Grade) (Dry) (discontinued **)
- Plenco 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
- Kolon DIAMAT® EG
- Ineos Nova 1504 High Heat Crystal Polystyrene
- UBE UBESTA® 3020LU1X3 Rigid Black Electronic Grade Nylon 12
- Elastomer Engineering Elastamide 300 Elastomer Modified RIM Nylon 6
- Ecomass® 4703ZC76 Stainless Steel Filled Polyurethane
- ChevronTexaco RPM® SAE 10W Heavy Duty Motor Oil
- ExxonMobil PP1024E4 Homopolymer
- Bulk Molding Compounds BMC 615 Mineral Filled, Glass Fiber Reinforced Polyester Compound
Copyright © lookpolymers.com All Rights Reserved