- Daikin DAI-EL G-781 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
Daikin DAI-EL G-781 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Daikin Industries |
| Trade Name | DAI-EL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daikin DAI-EL G-781 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Information provided by Daikin Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 32 @Temperature 121 °C |
32 @Temperature 250 °F |
ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | Peak value, at 25°C |
| Tensile Strength at Break | 14.8 MPa | 2150 psi | |
| Tensile Strength, Yield | 3.80 MPa @Strain 100 % |
551 psi @Strain 100 % |
|
| Elongation at Break | 220 % | 220 % | |
| Tear Strength | 20.9 kN/m | 119 pli | at 25°C |
| Compression Set | 8.0 % | 8.0 % | 70 hours at 25°C |
| 5.0 % @Temperature 100 °C |
5.0 % @Temperature 212 °F |
70 hours | |
| 8.0 % @Temperature 175 °C |
8.0 % @Temperature 347 °F |
70 hours | |
| 15 % @Temperature 200 °C |
15 % @Temperature 392 °F |
70 hours |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -14.5 °C | 5.90 °F | Gehman torsion test, T10 | |
| -10.0 °C | 14.0 °F | TR test, TR70 | |
| -7.00 °C | 19.4 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -18.0 °C | -0.400 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 5.50 min | 0.0917 hour | Curelastmeter |
Users viewing this material also viewed the following:
- MV Labs ND200 NdBr3·xH2O Neodymium bromide hydrate
- Ritelok TL71 Stud & Bolt Threadlocker
- Polymax® Maxelast® P3870H TPE, PP Overmold or Standalone use
- Mi-Tech Metals Thermitechâ„¢ CW85 85 Tungsten/15 Copper PM Metal Composite
- SABIC Innovative Plastics NORYL SE1GFN1 PPE+PS (Asia Pacific)
- Techmer ES HiFill® PA6/6 GF33 HS L BK001 33% Glass Filled
- Saint-Gobain Tygon® Norprene® A-60-F I.B. Pressure Tubing Formulation for CIP and SIP cleaning and sterilization systems
- Toyobo Vylopet® EMC145 Glass Reinforced Polyester, Standard Grade
- Clariant Renol 6642 2% Moly Nylon 66, Extrusion Grade, 2% Molybdenum Disulfide Lubricated
Copyright © lookpolymers.com All Rights Reserved