Star Plastics PC20NBR Molding Grade PC with Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Star Plastics, Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Star Plastics PC20NBR Molding Grade PC with Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Star Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | ASTM D638 |
| Tensile Modulus | 2.34 GPa | 340 ksi | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | 73°F, 0.125 in.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed, .125in; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 246 - 274 °C | 475 - 525 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 274 - 302 °C | 525 - 575 °F | |
| Nozzle Temperature | 274 - 302 °C | 525 - 575 °F | |
| Melt Temperature | 274 - 302 °C | 525 - 575 °F | |
| Mold Temperature | 71.1 - 98.9 °C | 160 - 210 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
Users viewing this material also viewed the following:
- Qualchem Danamid FEWL2-25 Polyamide 6, 25% Mineral Filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N990 (MT) Filler
- Kolon KOPA® KN173HI4 High Impact Nylon 6
- Less Common Metals Neodymium Vacuum Remelted Rare Earth Metal
- SABIC Innovative Plastics LNP THERMOCOMP ECF62 PEI (Asia Pacific)
- Suqian Unitechem Efficient Inhibitor 701
- A. Schulman ComAlloy Comtuf® 102 Polypropylene, Mineral Reinforced, Impact Modified
- Trelleborg Emerson & Cuming Stycast® 4640-25 Two-Component Silicone Flexible Encapsulant
- Aclo Accucomp ABS ABS803L Medium Impact Grade
Copyright © lookpolymers.com All Rights Reserved