SABIC Innovative Plastics LNP VERTON RV00CESS PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV00CESS PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* RV00CESS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ASTM D792 |
| 1.71 g/cc | 0.0618 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.440 % | 0.440 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 261 MPa | 37900 psi | ISO 527 |
| 270 MPa | 39200 psi | ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| 1.6 % | 1.6 % | ISO 527 | |
| Tensile Modulus | 19.65 GPa | 2850 ksi | 50 mm/min; ASTM D638 |
| 23.28 GPa | 3376 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 430 MPa | 62400 psi | ASTM D790 |
| 433 MPa | 62800 psi | ISO 178 | |
| Flexural Modulus | 18.02 GPa | 2614 ksi | ASTM D790 |
| 18.92 GPa | 2744 ksi | ISO 178 | |
| Izod Impact, Notched | 4.11 J/cm | 7.70 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1A |
| 43.0 kJ/m² @Temperature -40.0 °C |
20.5 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 102 kJ/m² | 48.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J | 13.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 18.0 J | 13.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.44 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 17.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.78 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 53.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 15 T 25 LTS PA6, 15% glass fibre, 25% mineral filling
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Mistron Vapor Filler
- Hong Kun Group UV Absorber
- Samsung Cheil Industries Starex® HR-0370F ABS, Unreinforced Heat Resistant
- Covestro Apec® HT KU 1-9333 High-Heat Polycarbonate
- ExxonMobil Mobiltrans AST
- DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66 (Unverified Data**)
- ATG s.r.l. CO-ECO Epichlorohydrin Rubber
- Atom Adhesives AA-BOND 2156 Epoxy Adhesive
- DuPont Performance Polymers Zytel® 80G33HS1L NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved