Aclo Accutech Polypropylene Copolymer CP0437M30CL Mica Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437M30CL Mica Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 40 | 40 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ASTM D638 |
| Flexural Strength | 25.0 MPa | 3630 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F |
Users viewing this material also viewed the following:
- Northstar Polymers MNB-013 Isocyanate Prepolymer
- Chevron Phillips Ryton® R10-110BL Polyphenylene Sulfide Compound (discontinued **)
- Materion BrushBronze® 630 (AMS 4640) 1.0" - 2.0"
- H.C. Starck Amperit® 704.072 Chromium Oxide (Cr2O3) 99.5%
- SABIC Innovative Plastics LNP THERMOCOMP WFB62 PBT
- Teknor Apex Sarlink® 3135 Thermoplastic Elastomer
- Zircar Zirconia BusterF Alumina Bulk Fiber Insulation
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- BASF Neopor® 5300 Expandable Polystyrene
- Cheng Yu Plastic A705G3 ABS 30% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved