LyondellBasell Lupolen® 6031 M HDPE, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Lupolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 6031 M HDPE, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flow, injection molding grade for fruit crates, tote boxes and bottle crates, cartridges, protective headgear, buckets, dishes, cartridges for adhesive film canisters, aerosol lids, child seats for automobiles, connector housings, cable clips.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 10.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
10.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 7.0 % | 7.0 % | |
| Tensile Modulus | 1.50 GPa | 218 ksi | |
| Tensile Impact Strength | 65.0 kJ/m² | 30.9 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 570 MPa | 82700 psi | |
| Tensile Creep Modulus, 1000 hours | 400 MPa | 58000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 135 µm/m-°C @Temperature 20.0 °C |
75.0 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | |
| Vicat Softening Point | 72.0 °C | 162 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
|
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Paratherm Corporation Paratherm™ NF Heat Transfer Fluid
- Parker Chomerics THERM-A-GAP™ G174 Cost Effective Gap Filler
- SABIC Innovative Plastics LNP Lubricomp ZFL36CCX PPE+PS
- SK Chemicals SKYTHANE® 870A T series Polyurethane
- Suqian Unitechem Light Stabilizer 944
- Borealis BorPURE™ MB6562 High Density Polyethylene for Injection Molding
- Azoty Tarnow™ Tarnamid® T-27 GB30 Polyamide 6 - Glass Beads Reinforced
- Bulk Molding Compounds BMC 1401 Encapsulating Material, Electrical Grade
- PolyOne Nymax™ GF 1800 33 BLACK 13 Nylon 612 with 33% Glass Fiber (discontinued **)
- Arkema Group KYNAR FLEX® 2850-00 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
Copyright © lookpolymers.com All Rights Reserved