Aclo Accutech Polypropylene CP0435G20CV Copolymer Glass Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene CP0435G20CV Copolymer Glass Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Approved to GMP.PP.029
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Ash | 18 - 22 % | 18 - 22 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
| Flexural Modulus | 2.499 GPa | 362.5 ksi | ASTM D790 |
| Izod Impact, Notched | 2.30 J/cm | 4.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 240 °F |
Users viewing this material also viewed the following:
- Nye Lubricants 868VH (FG) Synthetic Oil
- LG Chemical Lupox® PBT-HI1002F Impact Modified, Flame Retardant PBT Alloy
- Schott RG1000 Long Pass Filter
- Goodfellow Titanium 84/Molybdenum 16 Alloy
- Teknor Apex Telcar® TL-8730 Thermoplastic Elastomer
- A. Schulman POLYBLAK™ 3209 Superior Black Color Concentrate, 40% Carbon Black Based In Polypropylene
- Clariant PA131G2GN-91 Green Nylon 66, Highly Toughened
- CMW® D355F Pre-oxidized Silver Cadmium Oxide Contact Material ASTM B781 Table 3
- BASF Neopolen® P 9230 A 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved