Aclo Accutech Polyethylene HD0234G30UVL High Density Glass Reinforced UV Stabilized
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Glass fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polyethylene HD0234G30UVL High Density Glass Reinforced UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 52 | 52 | ASTM D785 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ASTM D638 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.699 GPa | 536.5 ksi | ASTM D638 |
| Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
| Flexural Modulus | 3.699 GPa | 536.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F |
Users viewing this material also viewed the following:
- PSM Industries PolyAlloys MIM-4605 sintered Low Alloy Steel
- LATI LARPEEK 50 G/30 30% Glass Reinforced Polyetheretherketone (PEEK) (Unverified Data**)
- Victrex® APTIV® 2102-100M Polyetheretherketone (PEEK) Polymer Film, Amorphous, Mineral Filled
- Huntsman PE1065 Film Extrusion Polyethylene (discontinued **)
- Karina White Color Concentrate for PVC
- Lucas-Milhaupt Premabraze 131 Gold Based Brazing Alloy
- Solvay Chemicals Allyl chloride 3-chloropropene
- Teknor Apex Telcar® TL-2580F Thermoplastic Elastomer
- Fainplast Compounds HAX HFX 024-15C Halogen Free PVC
- DuPont Performance Polymers Neoprene 654 Polychloroprene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved