- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Aclo Accutech ABS ABS832G10L Glass Reinforced
Aclo Accutech ABS ABS832G10L Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech ABS ABS832G10L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 0.60 g/10 min | 0.60 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.900 GPa | 420.6 ksi | ASTM D638 |
| Flexural Strength | 85.98 MPa | 12470 psi | ASTM D790 |
| Flexural Modulus | 3.699 GPa | 536.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.1 °C | 205 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C | 187 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 500 PC (Asia Pacific)
- Karina E 80/278-IS-RG Clear PVC Compound
- SYNTHOS Koplen® 0207 FR Expandable Polystyrene
- Samsung Cheil Industries Infino® AE-2130 PC/PET, Unreinforced
- Formosa Plastics Formolene® HF3728 Film (Hexene) HDPE
- Total PPH 5069 Polypropylene Homopolymer, Fiber
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, No Plasticizer
- UBE UBESTA® 3030U Nylon 12 (After Sodium Hydroide for 1000 hours)
- Kraton® D4150 K (O/E SBS) Linear Triblock Copolymer
Copyright © lookpolymers.com All Rights Reserved