SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* LF006 is a compound based on Polyetheretherketone resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| 1.537 g/cc | 0.05553 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
| 176 MPa | 25500 psi | ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 13.1 GPa | 1900 ksi | 1 mm/min; ISO 527 |
| 13.23 GPa | 1919 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
| 263 MPa | 38100 psi | ISO 178 | |
| Flexural Modulus | 10.75 GPa | 1559 ksi | ASTM D790 |
| 12.7 GPa | 1840 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.75 J/cm | 16.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 57.0 kJ/m² | 27.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 17.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.44 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 48.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| >= 298 °C @Thickness 3.20 mm |
>= 568 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 298 °C @Thickness 3.20 mm |
>= 568 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.780 mm |
V-0 @Thickness 0.0307 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6403 Adhesive
- Resinlab® EP1295 Black Medium Viscosity, Halogen Free, Flame Retardant Epoxy Casting Resin
- DuPont Performance Polymers Crastin® LW9020FR BK851 PBT (Unverified Data**)
- LG Chemical LUPOL HM5204 PP+MF20%, High Impact
- Schott D 263 Thin Borosilicate Glass
- Plenco 4548 Phenolic, Granular, Injection Molded
- Dow Corning SILASTIC® LS 5-8740 FLUOROSILICONE RUBBER BASE
- Dow Corning 1784 EMULSION
- Axiall 419-90D Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved