Aclo Accucomp ABS ABS802L High Impact Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Aclo Compounders |
| Trade Name | Accucomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accucomp ABS ABS802L High Impact Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 1.2 g/10 min | 1.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ASTM D638 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.900 GPa | 275.5 ksi | ASTM D638 |
| Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 4.38 J/cm | 8.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.2 °C | 189 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.2 °C | 171 °F | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL File #E56070 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EHB400A Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics GELOY FXW751SK ASA+PC (Asia Pacific)
- MarkeTech Yttrium Aluminate (YAlO3) Single Crystal Substrate
- Momentive Performance Materials Addisilâ„¢ 2050 E Industrial Extrusion Heat Cured Rubber
- MBA Polymers ABS 4124 Recycled acrylonitrile-butadiene-styrene copolymer
- Ensinger Tecapeek® XP98 XRO Polyetheretherketone (PEEK), compression molded, 30% carbon fiber filled, x-ray opaque
- Elastocon TPE Technologies Elastocon® 8088BL Thermoplastic Elastomer
- BASF Paliogen® Red Violet L 5100 Color Additive
- PolyOne Edgetek® PI-20GM-20CF/000 Polyetherimide (PEI), Carbon/Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved