A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.175 mm |
0.0040 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 169 MPa | 24500 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 225 MPa | 32700 psi | ASTM D790 |
| Flexural Modulus | 9.9133 GPa | 1437.8 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Radici Radilon® S RV200 (cond.) Nylon 6
- PolyOne Elastamax™ XL-2075 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Lucite International Diakon® ST45G6 Toughened Acrylic Polymer
- Taiwan PU Corporation TPUA-1560 TPU Shoe Adhesive
- Samyang Trirex® 3020PJ Polycarbonate
- SABIC Innovative Plastics NORYL GTX GTX909 PPE+PS+PA (Asia Pacific)
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 35% Cold Reduction
- Addiplast Addilene J 520 T30 Polypropylene Copolymer
- Eurofoam Porocell 251 BG NBR/PVC Foam
- PolyOne Edgetek® AS-10GB/000 Acrylonitrile Butadiene Styrene (ABS), Glass Bead Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved