- A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6
A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm |
0.0020 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 221 MPa | 32000 psi | ASTM D790 |
| Flexural Modulus | 8.818 GPa | 1279 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- ND Industries StudGrade® 146 Permanent StudGrade HD Threadlocker
- Parker Chomerics THERM-A-FORM 1641 Cure-in-Place Potting and Underfill Material
- Solvay Specialty Polymers Galden® D02 PFPE Fluid
- Saint-Gobain CHR® SG16-03(R) High Performance Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- UBE UBESTA® 3020GX6 Glass Fiber Reinforced Nylon 12
- EMS-Grivory Grivory® 2S 25 W 20 HL X black 9992 PA610
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 310ºF Cure Temperature
- E-Polymers EFLEX® S5070 Extrusion
- Fainplast Compounds PM 7005 Flexible PVC, Lead Free
- Overview of materials for Nylon 6, 10% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved