Hexcel® HexPly® F263 Epoxy Resin, T3T145 Carbon Tape

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F263 Epoxy Resin, T3T145 Carbon Tape.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: T_145-12"-F263; Various fibersInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 1260 MPa

@Temperature 177 °C
 183000 psi

@Temperature 351 °F
1362 MPa

@Temperature 24.0 °C
 197500 psi

@Temperature 75.2 °F
Tensile Modulus 125.7 GPa

@Temperature 177 °C
 18230 ksi

@Temperature 351 °F
132.3 GPa

@Temperature 24.0 °C
 19190 ksi

@Temperature 75.2 °F
Compressive Yield Strength 1154 MPa

@Temperature 71.0 °C
 167400 psi

@Temperature 160 °F
1333 MPa

@Temperature 24.0 °C
 193300 psi

@Temperature 75.2 °F
Shear Strength 68.0 MPa

@Temperature 177 °C
 9860 psi

@Temperature 351 °F
 Short Beam
72.0 MPa

@Temperature 132 °C
 10400 psi

@Temperature 270 °F
 Short Beam
111 MPa

@Temperature 24.0 °C
 16100 psi

@Temperature 75.2 °F
 Short Beam
124 MPa

@Temperature -54.0 °C
 18000 psi

@Temperature -65.2 °F
 Short Beam
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.15
Laminate
Dry Resin Content (%) 35-39
Prepreg
Fiber Volume (%) 55
Laminate
Flow (%) 11-24