SABIC Innovative Plastics NORYL GTX GTX8410W PPE+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX8410W PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow, 10% Glass Reinforced PPE+PA. Typically used in Automotive connectors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 36.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
36.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 94.0 MPa | 13600 psi | Nominal Stress, brk, Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.8 % | 3.8 % | Nominal Strain, 5 mm/min; ASTM D638 |
| Elongation at Yield | 3.6 % | 3.6 % | Nominal Strain, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.59 GPa | 521 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.10 GPa | 595 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| 0.370 J/cm @Temperature -30.0 °C |
0.693 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.85 J/cm | 9.09 ft-lb/in | ASTM D4812 |
| 4.96 J/cm @Temperature -30.0 °C |
9.29 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Dart Drop, Total Energy | 5.00 J @Temperature -30.0 °C |
3.69 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 124 µm/m-°C @Temperature -40.0 - 40.0 °C |
68.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 238 °C | 460 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Oceanchem Group Bromobutane (N-Butyl Bromide)
- Polimeri Europa Riblene® FC 26 Low Density Polyethylene - Blown Film Extrusion
- LNP Thermocomp® LF-1006 MG Polyetheretherketone, Glass milled Glass Fiber (discontinued **)
- S&E Specialty Polymers TufTech™ GA-1050 PVC Compound
- Ravago Manufacturing Americas Hylon® N1033STL Nylon 6/6 (Cond) (discontinued **)
- Gouda Vuurvast CURON 140 GM Dense Refractory Castable
- Kostat ICP-STAT ICD-1000 PC Sheet
- CeramTec ZN 40 Zirconia, ZrO2-MgO
- Beijing Evergrow Resources ASHRAE HEPA-W59 Glass Fiber Paper
- M. Holland Company LL106 LLDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved