Sumitomo Bakelite North America RXÂ® 1366FR-P Short-Glass Reinforced Diallyl Phthalate

Category	Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America RXÂ® 1366FR-P Short-Glass Reinforced Diallyl Phthalate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Short glass fiber reinforced, flame retardant, diallyl ortho-phthalate molding compound which meets the requirements of ASTM D5948 Type SDG-F.Information provided by Vyncolit, a Sumitomo Bak Group

Physical Properties	Metric	English	Comments
Density	1.87 g/cc	0.0676 lb/inÂ³	Relative Density; ASTM D792
Linear Mold Shrinkage	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	Compression Molding; ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	82.7 MPa	12000 psi	ASTM D638
Flexural Strength	131 MPa	19000 psi	At Rupture; ASTM D790
Flexural Modulus	12.4 GPa	1800 ksi	ASTM D790
Compressive Strength	152 MPa	22000 psi	ASTM D695
Izod Impact, Notched	0.427 J/cm	0.800 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	19.0 Âµm/m-Â°C @Temperature 20.0 Â°C	10.6 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM E-831
Thermal Conductivity	0.320 W/m-K	2.22 BTU-in/hr-ftÂ²-Â°F	ASTM C-518
Maximum Service Temperature, Air	170 - 180 Â°C	338 - 356 Â°F	UL 746B
Deflection Temperature at 1.8 MPa (264 psi)	204 Â°C	399 Â°F	As molded; ASTM D648
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	39 %	39 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.5 @Frequency 1e+6 Hz	3.5 @Frequency 1e+6 Hz	Wet; ASTM D150
	4.2 @Frequency 1000 Hz	4.2 @Frequency 1000 Hz	wet; ASTM D150
Dielectric Strength	17.7 kV/mm	450 kV/in	60Hz, Step-by-Step, wet; ASTM D149
Dissipation Factor	0.010 @Frequency 1000 Hz	0.010 @Frequency 1000 Hz	wet; ASTM D150
	0.016 @Frequency 1e+6 Hz	0.016 @Frequency 1e+6 Hz	wet; ASTM D150
Arc Resistance	130 sec	130 sec	ASTM D495
Comparative Tracking Index	>= 600 V	>= 600 V	IEC 112

Descriptive Properties	Value	Comments
Color	Black, Blue, Gray, Green, Dark Green, White
Flammability: Burning, sec	40	ASTM D229
Flammability: Ignition, sec	110	ASTM D229
Form	Granular
Main Filler	Glass Fiber
Molding Method	Compression, transfer, injection