Outokumpu 4306 Cr-Ni Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 4306 Cr-Ni Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 7.90 g/cc
0.285 lb/in³
RT
Mechanical Properties Metric English Comments
Hardness, Brinell 155
155
Outokumpu Typical, 20°C, Cold rolled strip/sheet; EN 10003-1
165
165
Outokumpu Typical, 20°C, Hot rolled plate (Quarto); EN 10003-1
Tensile Strength, Ultimate 580 MPa
84100 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
340 MPa

@Temperature 300 °C
 49300 psi

@Temperature 572 °F
 EN min.; EN 10002-5
360 MPa

@Temperature 200 °C
 52200 psi

@Temperature 392 °F
 EN min.; EN 10002-5
410 MPa

@Temperature 100 °C
 59500 psi

@Temperature 212 °F
 EN min.; EN 10002-5
Tensile Strength, Yield 200 MPa

@Strain 0.200 %
 29000 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
280 MPa

@Strain 0.200 %
 40600 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
320 MPa

@Strain 1.00 %
 46400 psi

@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
81.0 MPa

@Strain 0.200 %,
Temperature 500 °C
 11700 psi

@Strain 0.200 %,
Temperature 932 °F
 EN min.; EN 10002-5
89.0 MPa

@Strain 0.200 %,
Temperature 400 °C
 12900 psi

@Strain 0.200 %,
Temperature 752 °F
 EN min.; EN 10002-5
100 MPa

@Strain 0.200 %,
Temperature 300 °C
 14500 psi

@Strain 0.200 %,
Temperature 572 °F
 EN min.; EN 10002-5
109 MPa

@Strain 1.00 %,
Temperature 500 °C
 15800 psi

@Strain 1.00 %,
Temperature 932 °F
 EN min.; EN 10002-5
116 MPa

@Strain 1.00 %,
Temperature 400 °C
 16800 psi

@Strain 1.00 %,
Temperature 752 °F
 EN min.; EN 10002-5
118 MPa

@Strain 0.200 %,
Temperature 200 °C
 17100 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
127 MPa

@Strain 1.00 %,
Temperature 300 °C
 18400 psi

@Strain 1.00 %,
Temperature 572 °F
 EN min.; EN 10002-5
147 MPa

@Strain 1.00 %,
Temperature 200 °C
 21300 psi

@Strain 1.00 %,
Temperature 392 °F
 EN min.; EN 10002-5
147 MPa

@Strain 0.200 %,
Temperature 100 °C
 21300 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
181 MPa

@Strain 1.00 %,
Temperature 100 °C
 26300 psi

@Strain 1.00 %,
Temperature 212 °F
 EN min.; EN 10002-5
Elongation at Break 55 %
55 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Modulus of Elasticity 200 GPa
29000 ksi
RT
165 GPa

@Temperature 500 °C
 23900 ksi

@Temperature 932 °F
172 GPa

@Temperature 400 °C
 24900 ksi

@Temperature 752 °F
179 GPa

@Temperature 300 °C
 26000 ksi

@Temperature 572 °F
186 GPa

@Temperature 200 °C
 27000 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
 28100 ksi

@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
Hot rolled plate/Cold rolled strip/sheet, 10x10mm test pieces; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 100 °C
 8.89 µin/in-°F

@Temperature 212 °F
16.5 µm/m-°C

@Temperature 200 °C
 9.17 µin/in-°F

@Temperature 392 °F
17.0 µm/m-°C

@Temperature 300 °C
 9.44 µin/in-°F

@Temperature 572 °F
17.5 µm/m-°C

@Temperature 400 °C
 9.72 µin/in-°F

@Temperature 752 °F
18.0 µm/m-°C

@Temperature 500 °C
 10.0 µin/in-°F

@Temperature 932 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
20.0 W/m-K

@Temperature 400 °C
 139 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 18.2 %
18.2 %
Iron, Fe 71.68 %
71.68 %
Nickel, Ni 10.1 %
10.1 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000730 ohm-cm
0.0000730 ohm-cm