Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | ULTEM |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics Ultem ATX100F PEI+PCE.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D 792 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow | 6.0 g/10 min @Load 6.60 kg, Temperature 295 °C |
6.0 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D 1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D 638 |
Elongation at Break | 80 % | 80 % | Type I, 5 mm/min; ASTM D 638 |
Flexural Yield Strength | 106 MPa | 15400 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
Flexural Modulus | 2.53 GPa | 367 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
Izod Impact, Notched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
Izod Impact, Unnotched | 20.82 J/cm @Temperature 23.0 °C |
39.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 6.40 mm |
315 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
UL RTI, Electrical | 115 °C | 239 °F | UL 746B |
UL RTI, Mechanical with Impact | 115 °C | 239 °F | UL 746B |
UL RTI, Mechanical without Impact | 115 °C | 239 °F | UL 746B |
Flammability, UL94 | HB @Thickness 0.760 mm |
HB @Thickness 0.0299 in |
UL 94 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Comparative Tracking Index | 175 - 250 V | 175 - 250 V | PLC code 3; UL 746A |
Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC code 1; UL 746A |
High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |