CLAL-MSX NICLAL 1800 0 Annealed Copper Alloy, Free Cutting Nickel-Silver
| Category | Metal , Nonferrous Metal , Copper Alloy |
| Manufacturer | CLAL-MSX |
| Trade Name | NICLAL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CLAL-MSX NICLAL 1800 0 Annealed Copper Alloy, Free Cutting Nickel-Silver.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Main Characteristics: Good corrosion resistanceHigh mechanical propertiesTypical Applications:Parts subject to high stressHigh quality fastenersInformation provided by CLAL-MSX
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.75 g/cc | 0.316 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Vickers | <= 90 | <= 90 | |
| Tensile Strength, Ultimate | <= 440 MPa | <= 63800 psi | |
| Tensile Strength, Yield | >= 140 MPa @Strain 0.200 % |
>= 20300 psi @Strain 0.200 % |
|
| Elongation at Break | >= 35 % | >= 35 % | 100 A |
| Modulus of Elasticity | 130 GPa | 18900 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 100 °C |
8.89 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Specific Heat Capacity | 0.420 J/g-°C | 0.100 BTU/lb-°F | |
| Thermal Conductivity | 30.0 W/m-K | 208 BTU-in/hr-ft²-°F | |
| Melting Point | 1060 °C | 1940 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Copper, Cu | 62 % | 62 % | |
| Lead, Pb | <= 1.0 % | <= 1.0 % | |
| Nickel, Ni | 18 % | 18 % | |
| Zinc, Zn | <= 19 % | <= 19 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000260 ohm-cm | 0.0000260 ohm-cm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Silvery |
Users viewing this material also viewed the following:
- NYCOA 567 PA 6
- Lehmann & Voss LUVOCOM® 1105-7760 PEEK, with carbon fiber, PTFE, lubricant modified, high viscosity
- Huntsman Araldite GY 508 Bisphenol A Epoxy Liquid Resin
- Fujipoly Industries Sarcon® GR-n Gap Filler Pad
- Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes
- Techmer ES Statiblend® TPU G/CF40 40% Glass/Carbon Filled
- Borealis BG373MO Polypropylene Copolymer
- Total PPR 8573 Polypropylene, Film Extrusion Grade
- Elastocon TPE Technologies Elastocon® SMR1450 Thermoplastic Polyolefin Elastomer
- 3M 8891 Bond Breaker Tape
Copyright © lookpolymers.com All Rights Reserved