Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 13.0 - 16.0 kV/mm @Thickness 0.100 mm |
330 - 406 kV/in @Thickness 0.00394 in |
short term; ASTM D149 |
Polikim EFALON® C-25 PTFE, 25% Glass Filled C15 and C25 have less thermal expansion, higher wear resistance and less deformation under load compared to virgin Efalon® (PTFE). Applications: Seals, Seal rings, gaskets, valve sets, piston rings.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | ASTM D149 |
Premix Premi-Ject® 1102H Fiberglass Reinforced Thermoset BMC Premi-Ject® 1102H is a fiberglass reinforced thermoset bulk molding compound for coil encapsulation applications.Key features and benefits are:Designed with unique flow properties to encapsulate co.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | ASTM D149 |
Chevron Phillips Ryton® R10 5002C PPS Polyphenylene Sulfide
(discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol.. |
|||
Dielectric Strength | 13.0 - 22.0 kV/mm | 330 - 559 kV/in | Average value: 16.5 kV/mm Grade Count:6 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | ASTM D149 |
Plenco 5440 Black General Purpose Phenolic Molding Compound
(discontinued **) Plaslok 5440 is the replacement material for the former Union Carbide BMRS-5440. It is a two-stage, phenolic molding compound that has been successfully formulated to accommodate a very wide range .. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | 60°C for 500 hrs with 95% RH |
Fujipoly Industries Sarcon® 45U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | 150°C for 1,000 hrs; JIS-K-6249 |
Fujipoly Industries Sarcon® GR-Fd Gap Filler Pad Sarcon GR-d is a highly conformable, thermally conductive material in areas where space between surfaces is uneven and surface textures vary. GR-Fd has a mesh embedded overall.Information provided b.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | 60°C for 1,000 hrs with 90% RH; JIS-K-6249 |
Fujipoly Industries Sarcon® GR-HFd Gap Filler Pad Sarcon GR-d is a highly conformable, thermally conductive material in areas where space between surfaces is uneven and surface textures vary. GR-HFd has a hardened top surface and mesh embedded over.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | JIS-K-6249; ASTM D-149 |
Fujipoly Industries Sarcon® GR-L Gap Filler Pad Sarcon GR-L is a highly formable, thermally conductive gel material (no electicity conductive) in a versatile sheet form that easily fits and adheres to most all shapes and sizes of components, and .. |
|||
Dielectric Strength | 13.0 kV/mm @Thickness 3.00 mm |
330 kV/in @Thickness 0.118 in |
ASTM D149 |
Teknor Apex Beetle® MD21 Nylon 6, Extrusion Grade Notes: MD21 is a medium viscosity grade of nylon 6, designed for wire coating extrusion. MD21 is heavily pigment and is designed to provide good opacity even with thin coatings. It also features a.. |
|||
Dielectric Strength | 13.0 kV/mm @Thickness 3.00 mm |
330 kV/in @Thickness 0.118 in |
IEC 243 |
Sumitomo Bakelite North America RX® 611 Fiberglass Reinforced Phenolic RX 611 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type MFH.Information supplied by Sumitomo.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | AC |
Sapco C 220 Steatite Information provided by Sapco. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | ASTM D149-95a |
Thermoseal KLINGERSIL® C-6327 SBR Binder Gasketing Synthetic FiberModified SBR BinderControlled SwellUse for Low Temperatures and Low PressuresGood with Low Bolt LoadsInformation provided by Thermoseal Inc. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | |
Elastomer Engineering Elastamide 100 Elastomer Modified RIM Nylon 6 30% crystallinity. Information supplied by Elastomer Engineering. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | |
Elastomer Engineering Elastamide 150 Elastomer Modified RIM Nylon 6 29% crystallinity. Information supplied by Elastomer Engineering. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | |
Elastomer Engineering Elastamide 200 Elastomer Modified RIM Nylon 6 26% crystallinity. Information supplied by Elastomer Engineering. |
|||
Dielectric Strength | 13.0 kV/mm @Thickness 2.00 mm |
330 kV/in @Thickness 0.0787 in |
ASTM D149 |
Toyobo T-661 Nylon 66, Standard Grade (Conditioned) Features: Non-reinforced, Standard GradeInformation provided by Toyobo. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | Short Time; ASTM D149 |
Plenco 2571 Phenolic, Granular, Injection Molded PLENCO 02571 is a general purpose, organic filled phenolic molding compound offering optimum cure characteristics while maintaining excellent mechanical and electrical properties. UL recognized unde.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | Wet, Step by Step |
Cosmic Plastics E4905 Mineral Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | ASTM D149 |
Covestro Baydur® 726 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience .. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | DIN 53481 |
DSM Fibre Intermediates Nyrim® 1500 (Conditioned) Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | DIN 53481 |
DSM Fibre Intermediates Nyrim® 2000 (Conditioned) Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | Short Time |
Bulk Molding Compounds BMC 3001H Mineral Filled Alkyd BMC 3001H molding compound is a mineral filled, glass-fiber reinforced alkyd compound suitable for compression and transfer molding. Because of its soft flow, it is also used extensively in cold spu.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | Short Time |
Bulk Molding Compounds BMC 600 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 600 molding compound is a mineral filled glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a general purpose material with medium .. |
|||
Dielectric Strength | 13.0 kV/mm @Thickness 2.00 mm |
330 kV/in @Thickness 0.0787 in |
IEC 243-1 |
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | Wet, Step by Step |
Cosmic Plastics D33 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Dielectric Strength | 13.0 kV/mm | 330 kV/in | |
Quadrant EPP Duratron® PI D7015G PI, bearing grade (ISO Data) This grade contains 15 % graphite, added to provide long wear and low friction Good performance at elevated temperature (>425 °C) Good chemical resistance Easily machined from a broad range of shap.. |