Bulk Molding Compounds BMC 3001H Mineral Filled Alkyd

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Alkyd (Polyester), Molded, Mineral Filler
Manufacturer BMC - Bulk Molding Compounds Inc.
Trade Name BMC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bulk Molding Compounds BMC 3001H Mineral Filled Alkyd.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMC 3001H molding compound is a mineral filled, glass-fiber reinforced alkyd compound suitable for compression and transfer molding. Because of its soft flow, it is also used extensively in cold spur molding. This is a general-purpose material with good creep resistance and electrical properties.Typical applications include brush holders, voltage regulator housings and relay bases.
Physical Properties Metric English Comments
Specific Gravity 2.15 g/cc
2.15 g/cc
Water Absorption 0.19 %
0.19 %
24 hours, 23°C
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Mechanical Properties Metric English Comments
Hardness, Barcol 60 - 70
60 - 70
Flexural Strength 103 - 138 MPa
15000 - 20000 psi
Compressive Strength 145 - 172 MPa
21000 - 25000 psi
Izod Impact, Notched 1.07 - 2.14 J/cm
2.00 - 4.00 ft-lb/in
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Flammability, UL94 HB

@Thickness 6.35 mm
HB

@Thickness 0.250 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Dielectric Constant 6.7

@Frequency 60 Hz
6.7

@Frequency 60 Hz
Dielectric Strength 13.0 kV/mm
330 kV/in
Short Time
Dissipation Factor 0.020

@Frequency 60 Hz
0.020

@Frequency 60 Hz
Arc Resistance >= 180 sec
>= 180 sec
Comparative Tracking Index >= 500 V
>= 500 V
Processing Properties Metric English Comments
Mold Temperature 138 - 166 °C
280 - 330 °F