Electrical Properties | Metric | English | Comments |
---|---|---|---|
Insulation Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | Average value: 4.52e+10 ohm Grade Count:5 |
Overview of materials for Phenolic, Novolac, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral Filled". Each property range of values reported is minimum and maximum values.. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 1105-8382 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Highly dimensionally stable at ele.. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 1105-8476 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio.. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 1t-7503 Polyamide 6/6T, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 20-7324 Polyphthalamide, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 20-7913 Polyphthalamide, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low influence from moisture and temperature to measures and electrical prop.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 20-8112 Polyphthalamide, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 20-8114 Polyphthalamide, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 21-8113 Polyamide 6/6T, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 3-7723/ EG Polyamide 6, with carbon fiber, high viscosity Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressAntistatic.Handles, levers, rolle.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 50/CF/7/GF/20/TF/10/BK Polycarbonate, with carbon fiber, glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 65-8498 PP-copolymer, unreinforced Applications: Office communication.Reduced moment of inertia compared with metal parts.Dynamic stressed parts.Especially suitable for thin wall complex parts.Information provided by Lehmann & Voss &.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 80-7705 Polyacetal-copolymer, with carbon fiber, aramid reinforcement and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Suitable for discharging of st.. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | After 7 days |
Lord Adhesives CircuitSAFâ„¢ MA-420 Epoxy Surface Mount Adhesive CircuitSAFâ„¢ MA-420 is an epoxy surface mount adhesive that cures rapidly at elevated temperatures and has been designed for use in high speed printed circuit board assembly for the attachment o.. |
|||
Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
Lehmann & Voss LUVOCOM® 1105-7106 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Insulation Resistance | 1.00e+9 ohm | 1.00e+9 ohm | GB/T 10064-2006 |
Sichuan Deyang Haton® hCF31 Polyphenylene Sulfide Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Insulation Resistance | 1.00e+9 - 1.00e+10 ohm | 1.00e+9 - 1.00e+10 ohm | Dry; IEC 167 |
Vyncolit 4221 XB Novolac Phenolic Mineral and organic filled phenolic molding compound with good mechanical properties.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Insulation Resistance | 1.00e+9 - 1.00e+10 ohm | 1.00e+9 - 1.00e+10 ohm | Dry; IEC 167 |
Vyncolit 4421 XB Novolac Phenolic Mineral and organic filled phenolic molding compound with good mechanical properties.USES: Fuse holders, brush holders, circuit breakers, automotive ignition and solenoid covers.Information provided.. |
|||
Insulation Resistance | 1.00e+9 ohm @Diameter 8.00 - 10.0 mm |
1.00e+9 ohm @Diameter 0.315 - 0.394 in |
24hr/50°C+24h in water at 23°C; IEC; IEC/EN 61212-2 6.2 |
Elektro-Isola G-Etronax B Phenolic, Glass Fabric Reinforcement, Dark Brown, Tubes Description: Mechanical and electrical applications. High mechanical strength. Self-extinguishing, halogen-free. Good resistance to chemicals.Information provided by Elektro-Isola |
|||
Insulation Resistance | 1.00e+9 ohm @Thickness >=3.00 mm |
1.00e+9 ohm @Thickness >=0.118 in |
24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3 |
Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free.Applica.. |
|||
Insulation Resistance | >= 1.00e+9 ohm @Diameter 8.00 - 10.0 mm |
>= 1.00e+9 ohm @Diameter 0.315 - 0.394 in |
After immersion in water; IEC 1212-2 5.2 |
Hippe EP GC 21 Woven Glass Cloth Reinforced Epoxy Resin - Round, Rolled Tube Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at moderate temperatures. Very good stability of electrical properties when exposed to high relative .. |
|||
Insulation Resistance | >= 1.00e+9 ohm @Diameter 8.00 - 10.0 mm |
>= 1.00e+9 ohm @Diameter 0.315 - 0.394 in |
After immersion in water; IEC 1212-2 5.2 |
Hippe EP GC 22 Woven Glass Cloth Reinforced Epoxy Resin - Round, Rolled Tube Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at moderate temperatures. High mechanical strength at elevated temperatures. Very good stability of .. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | After immersion in water; IEC 1212-2 6.3 |
Hippe PF CP 205 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in electrical and electronic applications. Good stability of electrical properties under high humidity. Also available in cold or hot-punching versions. Flame retardant.Information provided .. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | After immersion in water; IEC 1212-2 6.3 |
Hippe PF CP 206 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in mechanical and electrical applications. Good electrical properties under normal humidity. Also available in hot-punching versions.Information provided by Hippe. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | After immersion in water; IEC 1212-2 6.3 |
Hippe PF CP 308 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in mechanical and electrical applications. Good electrical properties under normal humidity. Also available in hot-punching versions. Flame retardant.Information provided by Hippe. |
|||
Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | After immersion in water; IEC 1212-2 6.3 |
Hippe SI GC 202 Woven Glass Cloth Reinforced Silicone Resin - Sheet Used in mechanical and electrical applications at elevated temperature. Good heat resistance.Information provided by Hippe. |
|||
Insulation Resistance | 1.00e+9 ohm | 1.00e+9 ohm | Normal; ASTM D257 |
Chang Chun Plastic Longlite PM T308J General Purpose Phenolic Molding Compound ASTM Grade per ASTM D700 is 3.Information provided by Dowell Trading Company Ltd. |
|||
Insulation Resistance | 1.00e+9 ohm | 1.00e+9 ohm | After Boiling; ASTM D257 |
Chang Chun Plastic Longlite PM T355J Impact Phenolic Molding Compound ASTM Grade per ASTM D700 is 13.Information provided by Dowell Trading Company Ltd. |
|||
Insulation Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | Dry; IEC 167 |
Vyncolit X682 Novolac Phenolic Glass fiber, glass bead and graphite filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction.USES: Water pump seals and self-lubricating bearings.Info.. |
|||
Insulation Resistance | 1.00e+9 ohm | 1.00e+9 ohm | After Boiling; ASTM D257 |
Chang Chun Plastic Longlite PM T375J Heat Resistant Phenolic Molding Compound ASTM Grade per ASTM D700 is 13.Information provided by Dowell Trading Company Ltd. |