Overview of materials for Phenolic, Novolac, Mineral Filled

Category Polymer , Thermoset , Phenolic , Phenolic, Novolac, Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Phenolic, Novolac, Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.46 - 1.99 g/cc
0.0527 - 0.0719 lb/in³
Average value: 1.58 g/cc Grade Count:32
Water Absorption 0.0300 - 0.290 %
0.0300 - 0.290 %
Average value: 0.168 % Grade Count:25
Linear Mold Shrinkage 0.00180 - 0.00860 cm/cm
0.00180 - 0.00860 in/in
Average value: 0.00530 cm/cm Grade Count:32
Mechanical Properties Metric English Comments
Hardness, Rockwell E 70.0 - 91.0
70.0 - 91.0
Average value: 80.9 Grade Count:23
Tensile Strength, Ultimate 40.0 - 119 MPa
5800 - 17300 psi
Average value: 53.1 MPa Grade Count:32
Elongation at Break 0.310 - 1.70 %
0.310 - 1.70 %
Average value: 0.761 % Grade Count:32
Modulus of Elasticity 8.10 - 23.0 GPa
1170 - 3340 ksi
Average value: 10.8 GPa Grade Count:32
Flexural Yield Strength 55.0 - 240 MPa
7980 - 34800 psi
Average value: 92.9 MPa Grade Count:32
Flexural Modulus 6.00 - 21.0 GPa
870 - 3050 ksi
Average value: 9.46 GPa Grade Count:32
Compressive Yield Strength 152 - 434 MPa
22000 - 62900 psi
Average value: 199 MPa Grade Count:32
Poissons Ratio 0.270 - 0.350
0.270 - 0.350
Average value: 0.331 Grade Count:14
Shear Modulus 3.00 - 5.82 GPa
435 - 844 ksi
Average value: 3.73 GPa Grade Count:14
Izod Impact, Notched 0.138 - 0.243 J/cm
0.259 - 0.455 ft-lb/in
Average value: 0.169 J/cm Grade Count:23
Charpy Impact Unnotched 0.600 - 1.36 J/cm²
2.86 - 6.47 ft-lb/in²
Average value: 0.889 J/cm² Grade Count:8
Charpy Impact, Notched 0.150 - 0.450 J/cm²
0.714 - 2.14 ft-lb/in²
Average value: 0.211 J/cm² Grade Count:32
Thermal Properties Metric English Comments
CTE, linear 16.0 - 55.0 µm/m-°C
8.89 - 30.6 µin/in-°F
Average value: 35.9 µm/m-°C Grade Count:9
21.0 - 82.0 µm/m-°C

@Temperature 40.0 - 130 °C
11.7 - 45.6 µin/in-°F

@Temperature 104 - 266 °F
Average value: 50.5 µm/m-°C Grade Count:19
CTE, linear, Transverse to Flow 24.0 - 65.0 µm/m-°C
13.3 - 36.1 µin/in-°F
Average value: 46.1 µm/m-°C Grade Count:8
Thermal Conductivity 0.440 - 0.620 W/m-K

@Temperature 100 - 100 °C
3.05 - 4.30 BTU-in/hr-ft²-°F

@Temperature 212 - 212 °F
Average value: 0.510 W/m-K Grade Count:14
Maximum Service Temperature, Air 190 - 232 °C
374 - 450 °F
Average value: 208 °C Grade Count:24
Deflection Temperature at 1.8 MPa (264 psi) 150 - 250 °C
302 - 482 °F
Average value: 180 °C Grade Count:32
Deflection Temperature at 8.0 MPa 130 - 178 °C
266 - 352 °F
Average value: 147 °C Grade Count:7
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:31
Oxygen Index 26.4 - 45.0 %
26.4 - 45.0 %
Average value: 33.8 % Grade Count:20
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+11 - 2.10e+14 ohm-cm
1.00e+11 - 2.10e+14 ohm-cm
Average value: 1.05e+13 ohm-cm Grade Count:26
Insulation Resistance 1.00e+9 - 1.00e+11 ohm
1.00e+9 - 1.00e+11 ohm
Average value: 4.52e+10 ohm Grade Count:5
Dielectric Constant 4.40 - 6.10
4.40 - 6.10
Average value: 5.33 Grade Count:24
Dielectric Strength 6.90 - 30.0 kV/mm
175 - 762 kV/in
Average value: 14.3 kV/mm Grade Count:32
Dissipation Factor 0.0172 - 0.0820
0.0172 - 0.0820
Average value: 0.0514 Grade Count:24
Arc Resistance 137 - 188 sec
137 - 188 sec
Average value: 168 sec Grade Count:24
Comparative Tracking Index 150 - 225 V
150 - 225 V
Average value: 177 V Grade Count:32