Hippe SI GC 202 Woven Glass Cloth Reinforced Silicone Resin - Sheet
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Erhard Hippe KG |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hippe SI GC 202 Woven Glass Cloth Reinforced Silicone Resin - Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Used in mechanical and electrical applications at elevated temperature. Good heat resistance.Information provided by Hippe.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 - 1.90 g/cc | 1.60 - 1.90 g/cc | IEC 1212-2 8.1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | >= 90.0 MPa | >= 13100 psi | IEC 1212-2 5.7 |
| Flexural Strength | >= 120 MPa | >= 17400 psi | Perpendicular to laminations; IEC 1212-2 5.1 |
| Flexural Modulus | >= 13.0 GPa | >= 1890 ksi | IEC 1212-2 5.2 |
| Compressive Strength | >= 160 MPa | >= 23200 psi | Perpendicular to laminations; IEC 1212-2 5.3 |
| Shear Strength | >= 20.0 MPa | >= 2900 psi | Parallel to laminations; IEC 1212-2 5.6 |
| Izod Impact, Unnotched (ISO) | >= 26.0 kJ/m² | >= 12.4 ft-lb/in² | Parallel to laminations; IEC 1212-2 5.5.3 |
| Charpy Impact Unnotched | >= 2.50 J/cm² | >= 11.9 ft-lb/in² | Parallel to laminations; IEC 1212-2 5.5.2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 | V-0 | IEC 1212-2 7.2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | After immersion in water; IEC 1212-2 6.3 |
| Dielectric Constant | <= 6.0 @Frequency 48.0 - 62.0 Hz |
<= 6.0 @Frequency 48.0 - 62.0 Hz |
IEC 1212-2 6.2 |
| <= 6.0 @Frequency 1.00e+6 Hz |
<= 6.0 @Frequency 1.00e+6 Hz |
IEC 1212-2 6.2 | |
| Dielectric Breakdown | >= 25000 V @Temperature 90.0 °C |
>= 25000 V @Temperature 194 °F |
In oil, parallel to laminations; IEC 1212-2 6.2 |
| Dissipation Factor | <= 0.070 @Frequency 48.0 - 62.0 Hz |
<= 0.070 @Frequency 48.0 - 62.0 Hz |
IEC 1212-2 6.2 |
| <= 0.070 @Frequency 1.00e+6 Hz |
<= 0.070 @Frequency 1.00e+6 Hz |
IEC 1212-2 6.2 | |
| Comparative Tracking Index | >= 450 V | >= 450 V | IEC 1212-2 6.4 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Thermal Endurance | 180 T.I. | IEC 1212-2 7.1 |
| Water Absorption | < 75 mg | IEC 1212-2 8.2; Test piece 50 x 50 x 10 mm |
Users viewing this material also viewed the following:
- Covestro Petlon® DP3-1027 Semi-Crystalline PET, 45% Glass Fiber (discontinued **)
- Quadrant EPP Quadrant PC 1000 Extruded, Unfilled, Polycarbonate (ASTM Product Data Sheet)
- Hong Kun Group Iron(III) P-Toluene Sulfonate Pharmaceutical Intermediate
- Lucent Polymers ABS-305LG Acrylonitrile Butadiene Styrene, General Purpose, Low Gloss
- UBE UBESTA® 3030U Nylon 12 (After Nitric Acid (10%) for 1000 hours)
- Lubrizol ESTANE® 5707F1 Ester Based Thermoplastic Polyurethane (European Grade)
- 3M Scotch-Weld™ TL90 Threadlocker Anaerobic Adhesive
- Austin Novel Materials Texalan® 590A Polyether-based TPU
- Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved