- Polymer Property : Electrical Resistivity = 0.000132 ohm-cm
Polymer Property : Electrical Resistivity = 0.000132 ohm-cm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 900 °C |
0.000132 ohm-cm @Temperature 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 900 °C |
0.000132 ohm-cm @Temperature 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 30% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 900 °C |
0.000132 ohm-cm @Temperature 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC. This produces ASTM grain size 9.5. Other property values are ty.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain siz.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 700 °C |
0.000132 ohm-cm @Temperature 1290 °F |
|
| Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 900 °C |
0.000132 ohm-cm @Temperature 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 100 °C |
0.000132 ohm-cm @Temperature 212 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||