Haynes 242® alloy, hot rolled plate, annealed and aged

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 242® alloy, hot rolled plate, annealed and aged.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal stability, and resistance to high-temperature fluorine and fluoride environments. Applications include seal rings, containment rings, duct segments, casings, fasteners, rocket nozzles, pumps, hydrofluoric acid vapor containing processes, fluoroelastomer process equipment such as extrusion screws.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 9.05 g/cc
0.327 lb/in³
at RT
Mechanical Properties Metric English Comments
Hardness, Brinell 257
257
Converted from Vickers hardness
Hardness, Knoop 286
286
Converted from Vickers hardness
Hardness, Rockwell C 19
19
Converted from Vickers hardness
Hardness, Vickers 78.0

@Temperature 870 °C
78.0

@Temperature 1600 °F
140

@Temperature 760 °C
140

@Temperature 1400 °F
218

@Temperature 650 °C
218

@Temperature 1200 °F
263

@Temperature 540 °C
263

@Temperature 1000 °F
271

@Temperature 425 °C
271

@Temperature 797 °F
Tensile Strength, Ultimate 1270 MPa
184000 psi
280 MPa

@Temperature 980 °C
40600 psi

@Temperature 1800 °F
480 MPa

@Temperature 870 °C
69600 psi

@Temperature 1600 °F
730 MPa

@Temperature 760 °C
106000 psi

@Temperature 1400 °F
805 MPa

@Temperature 705 °C
117000 psi

@Temperature 1300 °F
945 MPa

@Temperature 650 °C
137000 psi

@Temperature 1200 °F
1000 MPa

@Temperature 540 °C
145000 psi

@Temperature 1000 °F
1060 MPa

@Temperature 425 °C
154000 psi

@Temperature 797 °F
1075 MPa

@Temperature 315 °C
155900 psi

@Temperature 599 °F
1110 MPa

@Temperature 205 °C
161000 psi

@Temperature 401 °F
1195 MPa

@Temperature 95.0 °C
173300 psi

@Temperature 203 °F
Tensile Strength, Yield 780 MPa

@Strain 0.200 %
113000 psi

@Strain 0.200 %
190 MPa

@Strain 0.200 %,
Temperature 980 °C
27600 psi

@Strain 0.200 %,
Temperature 1800 °F
275 MPa

@Strain 0.200 %,
Temperature 870 °C
39900 psi

@Strain 0.200 %,
Temperature 1600 °F
290 MPa

@Strain 0.200 %,
Temperature 760 °C
42100 psi

@Strain 0.200 %,
Temperature 1400 °F
450 MPa

@Strain 0.200 %,
Temperature 705 °C
65300 psi

@Strain 0.200 %,
Temperature 1300 °F
480 MPa

@Strain 0.200 %,
Temperature 540 °C
69600 psi

@Strain 0.200 %,
Temperature 1000 °F
525 MPa

@Strain 0.200 %,
Temperature 650 °C
76100 psi

@Strain 0.200 %,
Temperature 1200 °F
555 MPa

@Strain 0.200 %,
Temperature 425 °C
80500 psi

@Strain 0.200 %,
Temperature 797 °F
600 MPa

@Strain 0.200 %,
Temperature 315 °C
87000 psi

@Strain 0.200 %,
Temperature 599 °F
630 MPa

@Strain 0.200 %,
Temperature 205 °C
91400 psi

@Strain 0.200 %,
Temperature 401 °F
725 MPa

@Strain 0.200 %,
Temperature 95.0 °C
105000 psi

@Strain 0.200 %,
Temperature 203 °F
Elongation at Break 38.1 %
38.1 %
in 4D
30.9 %

@Temperature 705 °C
30.9 %

@Temperature 1300 °F
in 4D
37.7 %

@Temperature 650 °C
37.7 %

@Temperature 1200 °F
in 4D
39.8 %

@Temperature 95.0 °C
39.8 %

@Temperature 203 °F
in 4D
42.3 %

@Temperature 205 °C
42.3 %

@Temperature 401 °F
in 4D
42.7 %

@Temperature 315 °C
42.7 %

@Temperature 599 °F
in 4D
44 %

@Temperature 425 °C
44 %

@Temperature 797 °F
in 4D
46.6 %

@Temperature 540 °C
46.6 %

@Temperature 1000 °F
in 4D
56.1 %

@Temperature 870 °C
56.1 %

@Temperature 1600 °F
in 4D
65.1 %

@Temperature 980 °C
65.1 %

@Temperature 1800 °F
in 4D
66.3 %

@Temperature 760 °C
66.3 %

@Temperature 1400 °F
in 4D
Reduction of Area 46.6 %
46.6 %
30.4 %

@Temperature 705 °C
30.4 %

@Temperature 1300 °F
39.7 %

@Temperature 425 °C
39.7 %

@Temperature 797 °F
41.4 %

@Temperature 540 °C
41.4 %

@Temperature 1000 °F
41.5 %

@Temperature 315 °C
41.5 %

@Temperature 599 °F
41.8 %

@Temperature 650 °C
41.8 %

@Temperature 1200 °F
43.1 %

@Temperature 205 °C
43.1 %

@Temperature 401 °F
45 %

@Temperature 760 °C
45 %

@Temperature 1400 °F
46.9 %

@Temperature 870 °C
46.9 %

@Temperature 1600 °F
48.1 %

@Temperature 95.0 °C
48.1 %

@Temperature 203 °F
86 %

@Temperature 980 °C
86 %

@Temperature 1800 °F
Modulus of Elasticity 229 GPa
33200 ksi
RT
152 GPa

@Temperature 1000 °C
22000 ksi

@Temperature 1830 °F
163 GPa

@Temperature 900 °C
23600 ksi

@Temperature 1650 °F
172 GPa

@Temperature 800 °C
24900 ksi

@Temperature 1470 °F
185 GPa

@Temperature 700 °C
26800 ksi

@Temperature 1290 °F
193 GPa

@Temperature 600 °C
28000 ksi

@Temperature 1110 °F
199 GPa

@Temperature 500 °C
28900 ksi

@Temperature 932 °F
206 GPa

@Temperature 400 °C
29900 ksi

@Temperature 752 °F
213 GPa

@Temperature 300 °C
30900 ksi

@Temperature 572 °F
219 GPa

@Temperature 200 °C
31800 ksi

@Temperature 392 °F
225 GPa

@Temperature 100 °C
32600 ksi

@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 10.8 µm/m-°C

@Temperature 25.0 - 100 °C
6.00 µin/in-°F

@Temperature 77.0 - 212 °F
11.3 µm/m-°C

@Temperature 25.0 - 200 °C
6.28 µin/in-°F

@Temperature 77.0 - 392 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.000122 ohm-cm
0.000122 ohm-cm
RT
0.0001234 ohm-cm

@Temperature 100 °C
0.0001234 ohm-cm

@Temperature 212 °F
0.0001251 ohm-cm

@Temperature 200 °C
0.0001251 ohm-cm

@Temperature 392 °F
0.0001267 ohm-cm

@Temperature 300 °C
0.0001267 ohm-cm

@Temperature 572 °F
0.0001276 ohm-cm

@Temperature 1000 °C
0.0001276 ohm-cm

@Temperature 1830 °F
0.000128 ohm-cm

@Temperature 400 °C
0.000128 ohm-cm

@Temperature 752 °F
0.0001295 ohm-cm

@Temperature 500 °C
0.0001295 ohm-cm

@Temperature 932 °F
0.0001298 ohm-cm

@Temperature 900 °C
0.0001298 ohm-cm

@Temperature 1650 °F
0.0001306 ohm-cm

@Temperature 600 °C
0.0001306 ohm-cm

@Temperature 1110 °F
0.000132 ohm-cm

@Temperature 700 °C
0.000132 ohm-cm

@Temperature 1290 °F
0.0001324 ohm-cm

@Temperature 800 °C
0.0001324 ohm-cm

@Temperature 1470 °F