Ineos ABS Lustran® 452 (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS Lustran® 452 (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features:UnfilledSuitable processing methods:Sheet extrusionThermoformingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0383 lb/in³
Melt Flow	3.5 g/10 min @Load 10.0 kg, Temperature 220 °C	3.5 g/10 min @Load 22.0 lb, Temperature 428 °F	cm³/10 min.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	40.0 MPa	5800 psi
Elongation at Break	25 %	25 %	Nominal Strain
Elongation at Yield	3.6 %	3.6 %
Tensile Modulus	2.27 GPa	329 ksi

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	93.0 °C	199 °F
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL Recognized
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	UL Recognized

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Injection Molding
Mold Temperature	60.0 °C	140 °F	Injection Molding
Injection Velocity	200 mm/sec	7.87 in/sec
Injection Pressure	55.0 MPa	7980 psi